GE Engineering plastics Physical properties directory >> LEXAN™ PC >> EXL6414 Physical property table

[下載EXL6414物性表PDF] Consult EXL6414

Lexan PC EXL6414 Physical property

-40℃延展性,沖擊改良

Property

TYPICAL PROPERTIES ⁽¹⁾
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 50 mm/min	560	kgf/cm2	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	610	kgf/cm2	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	5.5	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	100	%	ASTM D 638
Tensile Modulus, 50 mm/min	17500	kgf/cm2	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	800	kgf/cm2	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	20300	kgf/cm2	ASTM D 790
Tensile Stress, yield, 50 mm/min	54	MPa	ISO 527
Tensile Stress, break, 50 mm/min	58	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	6	%	ISO 527
Tensile Strain, break, 50 mm/min	88	%	ISO 527
Tensile Modulus, 1 mm/min	2270	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	85	MPa	ISO 178
Flexural Modulus, 2 mm/min	2090	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	326	cm-kgf/cm	ASTM D 4812
Izod Impact, notched, 23°C	81	cm-kgf/cm	ASTM D 256
Izod Impact, notched, -30°C	70	cm-kgf/cm	ASTM D 256
Instrumented Impact Total Energy, 23°C	633	cm-kgf	ASTM D 3763
Instrumented Impact Total Energy, -30°C	622	cm-kgf	ASTM D 3763
Izod Impact, unnotched 80103 +23°C	NB	kJ/m2	ISO 180/1U
Izod Impact, unnotched 80103 -30°C	NB	kJ/m2	ISO 180/1U
Izod Impact, notched 80103 +23°C	70	kJ/m2	ISO 180/1A
Izod Impact, notched 80103 -30°C	60	kJ/m2	ISO 180/1A
Charpy 23°C, V-notch Edgew 80103 sp=62mm	70	kJ/m2	ISO 179/1eA
Charpy -30°C, V-notch Edgew 80103 sp=62mm	60	kJ/m2	ISO 179/1eA
Charpy 23°C, Unnotch Edgew 80103 sp=62mm	NB	kJ/m2	ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80103 sp=62mm	NB	kJ/m2	ISO 179/1eU
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	141	°C	ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed	136	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	122	°C	ASTM D 648
CTE, -40°C to 40°C, flow	7.02E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	7.2E-05	1/°C	ASTM E 831
CTE, 23°C to 80°C, flow	6.9E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	7.3E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	PASSES	-	IEC 60695-10-2
Vicat Softening Temp, Rate B/50	141	°C	ISO 306
Vicat Softening Temp, Rate B/120	140	°C	ISO 306
HDT/Be, 0.45MPa Edgew 120104 sp=100mm	136	°C	ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm	122	°C	ISO 75/Ae
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.19	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.4 - 0.8	%	SABIC Method
Mold Shrinkage, xflow, 3.2 mm	0.4 - 0.8	%	SABIC Method
Melt Flow Rate, 300°C/1.2 kgf	8	g/10 min	ASTM D 1238
Density	1.18	g/cm2	ISO 1183
Water Absorption, (23°C/sat)	0.35	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.15	%	ISO 62
Melt Volume Rate, MVR at 300°C/1.2 kg	7	cm210 min	ISO 1133
ELECTRICAL	Value	Unit	Standard
Arc Resistance, Tungsten {PLC}	5	PLC Code	ASTM D 495
Hot Wire Ignition {PLC)	2	PLC Code	UL 746A
High Voltage Arc Track Rate {PLC}	3	PLC Code	UL 746A
High Ampere Arc Ign, surface {PLC}	0	PLC Code	UL 746A
Comparative Tracking Index (UL) {PLC}	3	PLC Code	UL 746A
Volume Resistivity	1.7E+17	Ohm-cm	IEC 60093
Surface Resistivity, ROA	4.1E+17	Ohm	IEC 60093
Dielectric Strength, in oil, 3.2 mm	18	kV/mm	IEC 60243-1
Relative Permittivity, 1 MHz	2.6	-	IEC 60250
Dissipation Factor, 1 MHz	0.009	-	IEC 60250
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94HB Flame Class Rating (3)	1.47	mm	UL 94

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	3 - 4	hrs
Drying Time (Cumulative)	48	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	295 - 315	°C
Nozzle Temperature	290 - 310	°C
Front - Zone 3 Temperature	295 - 315	°C
Middle - Zone 2 Temperature	280 - 305	°C
Rear - Zone 1 Temperature	270 - 295	°C
Mold Temperature	70 - 95	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm

[下載EXL6414物性表PDF] Consult EXL6414

Physical properties of related products: 1173X BX9349 EX7631T EXL1330 EXL9330 EXL9132 EXL9134 EXL9335 EXL1414 EXL4419 EXL1414H EXL1132 ML7667 EXL1413T ML6413 ML6411 ML6412 EXL1494T EXL1463T EXL1433T EXL1414T EXL1443T EXL1434T EXL1434 EXL9112 EXL5689 EXL1162T EXL1132T EXL1810T EXL4016H EXL1192C EXL8414 EXL1483T EXL1484T EXL1036 EXL1493T EXL1182T EXL1890T EXL1112T EXL1112 EXL8134 EXL8454 EXL8483 EXL9330S EX1632T

Correlation search: EXL6414-111 EXL6414-701 EXL6414-BK1066 EXL6414-NA Lexan EXL6414 EXL6414物性 Sabic EXL6414 GE EXL6414 PC EXL6414 GE PC 聚碳酸酯 Sabic PC PC 塑膠原料

廣州華秀塑膠有限公司不僅是專業的Lexan PC EXL6414原料供應商，亦注重技術支持及全方位的解決方案，提供從材料鑒定、模具設計、成型加工等系列幫助，亦可為客戶量身定制各特殊性能之Lexan PC EXL6414材料，進而協助客戶提高產品竟爭力。

聯絡我們

地址:廣州市天河區中山大道中439號東圃天銀商貿大廈1720-1723室

電話:020-82582555

傳真:020-82523699

Email: sales@va-so.cn

Lexan PC EXL6414報價 >>

常規產品

長纖增強尼龍66 長纖增強PPA
長纖增強尼龍6 長纖增強PP
長纖增強復合材料沖擊改性復合尼龍66
沖擊改性復合尼龍6 高強尼龍
沖擊改性復合尼龍沖擊改性復合材料
改性PP 改性的合金料
高溫改性塑料含氟聚合物
改性POM 改性PBT
改性PC 焊接用復合塑料
高比重復合塑料永久防靜電塑料
永久防靜電ABS 永久防靜電合金
永久防靜電POM 其他導電材料
導電尼龍導電PE,導電PP
高溫導電塑料導電POM
導電PBT 導電PC
其他非PTFE自潤滑塑料非PTFE自潤滑PA
非PTFE自潤滑聚苯醚非PTFE自潤滑PPA
非PTFE自潤滑聚甲醛非PTFE自潤滑聚碳酸酯
其他潤滑塑料潤滑尼龍
潤滑烯烴潤滑PPO(PPE+PS)
耐熱潤滑塑料潤滑POM
潤滑PBT 潤滑彈性體
潤滑PC 擠出PBT
熱傳導復合塑料其他PC
EMI/RFI屏蔽復合塑料預著色非填充樹脂

Lexan PC EXL6414

華秀塑膠為您提供詳細的Lexan PC EXL6414物性表參數。

華秀塑膠為您提供詳細的Lexan PC EXL6414物性表參數。